Chrome bricks are neutral bricks, mainly used as an isolation layer for acidic and alkaline refractories at high temperatures, and also used as the lining of non-ferrous smelting furnaces.
لكن, it should not be used in direct contact with the iron and the atmosphere changes frequently.
Chrome brick in the glass melting kiln began to be used. But only limited to dark bottles and jars glass kiln or alkali-free glass fiber kiln.
And mainly used in the high-temperature parts of the glass kiln. Such as the upper pool wall, small furnace mouth, ثقب السائل المتدفق, charging mouth, وأماكن أخرى, because it can significantly extend the kiln age.
PER company produces high-quality refractory bricks including refractory clay bricks, طوب حراري عالي الألومينا, طوب السيليكا المقاوم للحرارة, طوب حراري المغنيسيا, طوب موليت, طوب العزل, إلخ.
في أثناء, if you are interested in our منتجات الطوب الحراري, أو إذا كنت تخطط لبناء فرن أو فرن, يمكنك الاتصال بنا! سوف نقوم بالرد عليك على الفور بتقديم المشورة المهنية وبأسعار تنافسية!

More Chrome Bricks Types

طوب الألمنيوم والكروم

طوب الألمنيوم والكروم

طوب AlCr عبارة عن طوب عالي الألومينا مع Al2O3 كمكون رئيسي وكمية صغيرة من Cr2O3.
The sintered brick made of AlCr slag is also AlCr brick, also called AlCr slag brick. طوب الألمنيوم والكروم يفوق مقاومة تآكل طوب الألومينا العالية, طوب خبث الألمنيوم والكروم, والخصائص الميكانيكية ذات درجة الحرارة العالية ذات الخصائص الجيدة.
يتميز طوب AlCr بالعديد من المزايا مثل الكثافة العالية, مسامية منخفضة, قوة السندات عالية, صلابة عالية, نعومة الحمل العالية, مقاومة تآكل جيدة, مكافحة تجوب, مقاومة جيدة للصدمات الحرارية, مقاومة قوية لذوبان المعادن وتآكل الخبث, حياة طويلة, إلخ.
والذي يستخدم على نطاق واسع في معدات الصهر المختلفة وغيرها من الأفران ذات درجات الحرارة العالية جدًا.

Magnesium Chrome Brick

Ordinary magnesia-chromium brick is made of sintered magnesia sand and chromite as raw materials, in appropriate proportion, by forming and high-temperature firing.
The mineral composition of the product is magnesite, الإسبنيل, وكمية صغيرة من السيليكات.
Ordinary magnesia-chromium brick has good resistance to alkaline slag, better resistance to acid slag than magnesia brick, better resistance to thermal shock than magnesia brick, higher load softening temperature, and good volume stability at high temperature, small shrinkage of the refired line at 1500℃.
Magnesium aluminum brick has good slag resistance, high-temperature performance, and thermal stability, the price is cheaper than magnesium spinel brick.
They are widely used in the roof of steelmaking flat furnaces and are still used in steel ladles, steelmaking furnace linings, glass kiln heat storage chambers, mixed iron furnaces, copper reflex kiln roofs, and refractory industry high-temperature kilns.

Types and Characteristics of Magnesium-Chromium Bricks

حالياً, there are several types of magnesium chrome brick produced through different methods, including common brick, direct bonding brick, common sintered brick, re-bonding brick, and fusion casting brick.

1. Common Magnesia Chrome Brick

This is the traditional product, with chrome ore as coarse particles and magnesium sand as a fine powder. Or two materials using graded particle composition, the firing temperature is generally 1550 ~ 1600 ℃. The microstructure of this brick shows little direct combination between chromite particles and magnesite, mostly silicate (CMS) cementation or fissure isolation. Fang magnesite in the desolvation phase less, the matrix is rarely directly combined, the mechanical properties of this brick are poor, poor resistance to slag corrosion.

2. Directly Combined Magnesia-Chromium Brick

Directly combined with magnesium-chromium brick is developed based on ordinary magnesium-chromium brick. Its production characteristics are mainly two points, one is the use of more pure raw materials, and the second is the use of higher firing temperature. The so-called direct bonding means that there is more direct contact between chromite particles and magnesite in the brick. Because there is less Si02 in the raw material (controlled below 1% إلى 2%), less silicate is generated. Then the silicate is extruded into the corner of the solid phase particles using high-temperature firing, thus improving the direct bonding of the solid phase.
Direct bonding magnesium-chromium brick due to the high degree of direct bonding, so that the brick has a high-temperature strength, slag resistance, مقاومة التآكل, scouring resistance, المقاومة للتآكل, and excellent thermal shock stability and volume stability at 1800 ℃.

3. Common Sintered Magnesium-Chromium Brick

This product production process is characterized by a certain ratio of magnesium sand and chromite fine powder mixture of high-temperature combustion. To achieve the generation of secondary spinel and magnesia-chromite direct bonding for solid-phase reaction, the production of common sintering material. This material is used to manufacture sintered products or chemically bonded products.
Co-sintered magnesia-chromium bricks have better direct bonding and microstructural homogeneity than directly bonded bricks, with more magnesite desolvation phase and intergranular secondary spinel, co-sintered magnesia-chromium bricks have a series of better properties than directly bonded bricks, especially known for high-temperature strength, resistance to rapid temperature change and slag resistance.

4. Combined Magnesium-Chromium Brick

Electric fusion method to make magnesium-chromium mixed powder melt, through the melt precipitation crystal, the formation of a fairly uniform microstructure, magnesium-chromium spinel, and magnesite mixed crystal as the main phase composition of the raw material, the electric fusion magnesium-chromium material crushed into certain particle size, mixed molding, by firing to prepare the combined brick, or directly used to do chemically bonded brick.

حول شركة الحراريات PER

PER Refractories Company is located in Xinmi City, مقاطعة خنان, مسقط رأس المواد الحرارية في الصين. شركتنا هي مؤسسة حرارية قائمة على التكنولوجيا تدمج R.&د, إنتاج, مبيعات, والخدمات الفنية. توفر الموارد الغنية والجودة الممتازة في الإقليم ظروفًا ممتازة لا مثيل لها إنتاج المواد الحرارية. منتجاتنا الرئيسية هي الطوب الطيني الحراري, طوب حراري عالي الألومينا, طوب السيليكا المقاوم للحرارة, طوب حراري المغنيسيوم, طوب موليت, طوب العزل, وغيرها منتجات مقاومة درجات الحرارة العالية.

شركة PER للحراريات هي قاعدة إنتاج الأخضر, توفير الطاقة, ومواد حرارية جديدة صديقة للبيئة. لقد حصلت شركتنا على شهادة ISO9001:2008 شهادة نظام الجودة الدولية و GB / T24001-2004 / ISO14001:2004 شهادة نظام الإدارة البيئية, شهادة وكالة فحص جودة المؤسسة. منتجاتنا تباع بشكل جيد في أكثر من 20 دول في جميع أنحاء العالم. هم المنتجات الحرارية المفضلة لعلم المعادن, غير حديدية, البتروكيماويات, زجاج, سيراميك, وغيرها من الصناعات الحرارية.

    اترك طلبك للحصول على الطوب الحراري وطوب العزل! سوف نقوم بالرد في 24 ساعات.

    اسمك(مطلوب):

    بريدك الالكتروني(مطلوب):

    الهاتف الخاص بك:

    رسالتك(مطلوب):

    البرنامج المساعد للمشاركة الاجتماعية في ووردبريس مدعوم من Ultimatelysocial

    الإشتراك!