01. Silica fire brick is an acid-refractory material, mit guter Beständigkeit gegen saure Schlackenerosion, und Ladungserweichungstemperatur von bis zu 1640 ~ 1670 ℃, the volume of long-term use at high temperatures is relatively stable.
02. It is mainly used in the partition wall of the charring room and combustion room of the coke oven, the heat storage room and slagging room of the steel-making flat furnace, equalization furnace, refractory material of the glass melting kiln and ceramic firing kiln, usw., and other load-bearing parts of the kiln’s vaults and so on. It is also used in the high-temperature load-bearing part of hot blast furnaces and the roof of acid-flat furnaces.
03. It is mainly acidic refractory material composed of scaled quartz, quadratischer Quarz, and a small amount of residual quartz and glass phase. Silicon dioxide content of 94% oder mehr. True density 2.35g/cm3.
Resistant to acidic slag erosion. Höhere Warmfestigkeit. Die Starttemperatur für die Enthärtung der Ladung beträgt 1620–1670 °C. Keine Verformung bei hoher Temperatur für Langzeitgebrauch. Geringe Thermoschockstabilität (Der Wärmeaustausch in Wasser beträgt das 1- bis 4-fache).
Natural silica as raw material, plus einer angemessenen Menge Mineralisierungsmittel, to promote the transformation of quartz in the body of the blank to, scale quartz. Langsam unter reduzierender Atmosphäre abgefeuert 1350 ~ 1430 ℃.
Heizung auf 1450 ℃ ungefähr 1.5 ~ 2.2% of the total volume expansion, Durch diese Restdehnung werden die Fugen geschlossen, um sicherzustellen, dass der Mauerwerkskörper eine gute Luftdichtheit und strukturelle Festigkeit aufweist.
Scalar quartz, argillaceous quartz, and residual quartz have large changes in volume at low temperatures due to changes in crystal type, so the thermal stability of silica bricks at low temperatures is poor.
During use, it should be heated and cooled slowly below 800℃ to avoid cracks. daher, should not be used in 800 ℃ below the temperature of the rapid change in the kiln.
04. The nature and process of silica bricks are closely related to the crystalline transformation of SiO2. daher, the true specific gravity is an important quality indicator of silica bricks.
General requirements in 2.38 or less, high-quality silica refractory bricks should be 2.35 or less. True specific gravity is small, reflecting the brick in the number of scale quartz and square quartz, residual quartz amount is small, so the residual linear expansion is small, and the use of strength decline is also less.
Silicon dioxide has seven crystalline variants and one amorphous variant. These variants can be divided into two categories: the first type of variant is quartz, quartz, und Quarz, their crystalline structure is very different, and the transformation between each other is very slow. The second type of variant is a subspecies of the above variants – α β and γ type, their structure is similar, and the transformation between each other is faster.
05. The raw material for the manufacture of silica bricks is silica. In Silica raw materials, the higher the SiO2 content, the higher the refractoriness. The most harmful impurities are Al2O3, K2O, Na2O, usw., they seriously reduce the refractoriness of refractory products.
Silica bricks are made from silica with SiO2 content of not less than 96%, adding mineralizing agent (z.B., iron scale, milk of lime) and binding agent (z.B., molasses, sulfite pulp waste liquid), and produced by mixing, Formen, Trocknen, and sintering processes.
Silica bricks are mainly used in coke ovens, glass furnaces, acid steel furnaces, und andere thermische Geräte. The following two points should be noted when using silica bricks:
1. When the silica product is at 200~300℃ and 573℃, the volume will expand suddenly due to crystal transformation. daher, when baking, the temperature rise below 600℃ should not be too fast, and drastic temperature changes should be avoided when cooling to below 600℃.
2. Avoid contact with alkaline slag as much as possible.
Silica fire bricks for coke ovens are a kind of silica refractory material used to build coke ovens with quartz crystals. Silica bricks for coke oven should have the following characteristics:
1. High load softening temperature. Silica brick for coke oven should be able to withstand the dynamic load of coal loading truck at high temperatures at the top of the furnace, and not be deformed in long-term use. daher, the Coke oven silica brick load softening temperature requirements are high.
2. High thermal conductivity. Coke is made from coking coal in the carbonization chamber by conducting heat in the combustion chamber wall. daher, the silica bricks used to build the combustion chamber wall should have high thermal conductivity.
3. Gute Temperaturwechselbeständigkeit. As the coke oven needs to be regularly loaded and coke discharged, the temperature of the silica bricks on both sides of the combustion chamber will change dramatically, so the coke oven silicon bricks are required to have good thermal expansion.
4. High-temperature volume stability.
Silica brick for glass kilns is quartz as the main component of silica refractory materials, used in the construction of glass kiln high-temperature components. Silica bricks for glass kilns should have the following characteristics:
1. Stable high-temperature volume, the furnace body will not change due to temperature fluctuations.
2. No pollution to the glass liquid.
3. Beständig gegen chemische Erosion.
4. Geringe Schüttdichte.
PER Refractories company produces a large amount of silica brick, many varieties, mainly used in coke ovens, carbonization chambers, combustion chambers and partition walls and glass kiln roofs, kiln pools. There are also high-temperature load-bearing parts of the hot blast stove, carbon roasters, and other kilns that also use alumina silica bricks for the lining.
Seit Oktober, Die Preise für Aluminiumoxid sind weiter gestiegen, and China's largest bauxite importer - a…
Erste, Ziegel mit hohem Tonerdegehalt: The Leader In High Temperature Refractories As a leader in high-temperature…
The application of refractory bricks in the kiln immediately endangers the operation rate of the…
Analysis Of The Causes Of Common Quality Problems In Tunnel Kiln Construction And Measures To…
Corundum quality refractory castables are made from corundum to the new jade refractory insulation material…
Analyse feuerfester Aluminium-Silizium-Rohstoffe Prof. Li Yong of the University of Science and…