Peran Kulit Kiln di Rotary Kiln

Kulit Kiln Terbuat Dari Klinker Atau Debu Dari Fase Cair Maupun Semi Cair Menjadi Padat.

Fungsi Utamanya Adalah

1. Lindungi batu bata tahan api dari suhu tinggi langsung dan erosi kimia.
2. Menyimpan energi panas, mengurangi kehilangan panas dari cangkang kiln ke area sekitarnya, dan meningkatkan efisiensi termal tanur putar.
3. Bertindak sebagai media perpindahan panas, menyerap panas secara radiasi atau konveksi ketika cangkang kiln terkena udara dan bersentuhan dengan udara panas, dan memindahkan panas ke bahan mentah secara konduksi ketika cangkang kiln bersentuhan dengan bahan di bagian bawah.
4. Permukaan kulit kiln kasar, hal ini dapat mengurangi laju aliran bubuk dan memperpanjang waktu reaksi material di dalam kiln.

The Main Factors Affecting The Generation Of Kiln Skin

1. The Chemical Composition Of The Material

Kiln skin is the product of the process of turning the liquid phase into the solid phase. Aluminum and iron composition is more, the amount of liquid phase is more, easy to form the kiln skin. The composition of aluminum and iron is less, the amount of liquid phase is less, and the formation of kiln skin is more difficult. With more aluminum in the raw material, the viscosity of the liquid phase is large, forming the kiln skin is more difficult, but once formed, it is more solid. With more iron in the raw material, the viscosity of the liquid phase is smaller, and the kiln skin is easy to form, but the formed kiln skin also easy to falls off.

2. The Temperature Of The Flame

With low flame temperature, the liquid phase formed by the material is less, not easy to form the kiln skin, flame temperature is too high, it will make the kiln skin temperature higher than the solidification temperature of the liquid phase, and the kiln skin is easy to fall off.

3. The Shape Of The Flame

The temperature of the kiln skin is affected by the shape of the flame, as well as the heat dissipation of the kiln shell cylinder. Secara umum, too short, too sharp, too thick, and wide flame erosion of the kiln skin is more harmful, long flame is more favorable to the kiln skin, but will make the kiln heat dispersion, bad for firing.
Karena itu, during operation, we must maintain a certain reasonable flame shape and position, strictly control the clinker caking, prevent the caking of large blocks to wash the kiln skin, stabilize the kiln’s thermal regime, prevent caking, and find large blocks or caking to deal with in time.

Kiln Skin Shedding And Redness

Kiln skin will fall off because the temperature exceeds its solidification temperature, and sometimes it will also fall off with the firebrick because of uneven heating, the main reasons for falling off are
1. unstable feed composition and feeding quantity or fluctuating output, resulting in unstable kiln temperature If the feeding material is good for a while, the kiln temperature is high, and when it is not, the temperature is low. When the amount of material is high, the temperature is low, and when the amount of material is low, there is no material to absorb more than the heat. Lewat sini, the temperature is high and low, resulting in uneven thermal expansion and contraction of the kiln skin, easy to fall off.
2. wrong operating procedures mainly due to improper adjustment of the shape of the flame.

When you find that the kiln skin is falling off, you can judge it by checking the kiln shell temperature in the central control room.
Umumnya, the temperature of the kiln shell is around 200-300 degrees, and if the temperature is too high, there is a possibility that the kiln skin will fall off.
Pada saat ini, you should immediately remedy the kiln skin measures, immediately reduce the amount of coal injection, or change the shape and position of the flame.
At the site, you can use a blower or compressed air to cool the kiln shell that has fallen off.
The blower should be placed at the four or eight o’clock position (where the material flow is), as close as possible to the area where the kiln skin has fallen off.

The shedding of kiln skins can be very damaging to the rotary kiln’s resistant material, and to make it last longer, it is more important to reduce the fluctuations in the production of the rotary kiln, including the medium, suhu, and output.

Jadi, What Are The Requirements and Types Of Refractory Bricks Used in Cement Rotary Kilns?

Refractory bricks should have strong chemical resistance. During the operation of the cement rotary kiln, it will be subject to wear and erosion of clinker residue, so the refractory bricks should have a strong resistance to chemical erosion.

In different parts of the cement rotary kiln, the atmosphere and working temperature are different, so the refractory bricks used in different parts of the rotary kiln, such as the decomposition zone, transition zone, and cooling zone, juga berbeda.

At this stage, the following types of refractory bricks are used in rotary kilns.
Cement rotary kiln commonly used refractory bricks are batu bata alumina tinggi, magnesium-chromium bricks, magnesia-alumina spinel bricks, magnesia-iron spinel bricks, dll..

The higher the alumina content of high alumina brick, the stronger the resistance to acid and alkaline chemical slag erosion. Generally used in cement rotary kiln firing belts and other places.
Magnesia-chromium brick is mainly composed of spinel and magnesite. Magnesia-chromium brick has the characteristics of high refractoriness, strong resistance to alkaline slag erosion, and good thermal stability. It is generally used in the firing zone of a cement kiln.
Magnesia-alumina spinel brick is made of high-purity magnesia sand and aluminum ore by batching, percampuran, and pressing. It has good thermal shock resistance and reduction resistance. The cement kiln transition zone generally uses magnesia spinel.
Magnesia-iron spinel brick is a kind of chrome-free characteristic of the environment beneficial pollution is very little, excellent thermal shock stability, good hanging kiln skin ability, erosion resistance is also very good, low thermal conductivity and thermal expansion, and good structural flexibility. In the real production application, the service life of magnesia iron spinel brick is more than 12 months.
Dolomite brick has a low price, in the price is not high at same time its hanging kiln skin sex is also quite recognized by the industry. In the rotary kiln firing zone, the free f-CaO in the dolomite brick reacts with the C2S in the cement clinker to produce the high melting point C3S, which allows the brick to have a stable kiln skin adhering to the hot surface.

Under the rapid development of the world cement industry, PER Refractories has produced refractory bricks for cement kilns that have made significant progress in both type and quality. We offer a wide range of high-quality refractory products.

xla2l

Tulisan Terbaru

“Peristiwa Black Swan” di Guinea Memicu Harga Alumina

Sejak Oktober, harga alumina terus meningkat, and China's largest bauxite importer - a…

2 months ago

Batu Bata Alumina Tinggi: Penjaga Kokoh Sektor Suhu Tinggi

Pertama, Bata Alumina Tinggi: The Leader In High Temperature Refractories As a leader in high-temperature…

2 months ago

Kerusakan Dan Perbaikan Batu Bata Tahan Api Di Rotary Kiln Semen

The application of refractory bricks in the kiln immediately endangers the operation rate of the…

1 year ago

Apa Masalah Kualitas Umum Dalam Konstruksi Tunnel Kiln?

Analysis Of The Causes Of Common Quality Problems In Tunnel Kiln Construction And Measures To…

1 year ago

Terbuat Dari Apa Bahan Castable Tahan Api Korundum?

Corundum quality refractory castables are made from corundum to the new jade refractory insulation material…

1 year ago

Perkembangan Terkini Bahan Baku Tahan Api Aluminium-Silikon

Analisa Bahan Baku Tahan Api Aluminium-Silikon Prof. Li Yong of the University of Science and…

1 year ago