Хайлсан цутгамал муллит тоосго are made of high-quality mullite clinker as raw material, which is melted and cast at high temperatures in an electric arc furnace.
The refractory fire bricks are characterized by dense crystal structure, өндөр ачаалал зөөлрүүлэх температур, дулааны цохилтод сайн тэсвэртэй, high mechanical strength at room temperature and high temperature, good abrasion resistance, сайн дулаан дамжуулалт, and strong resistance to slag corrosion, гэх мэт. The bricks are widely used in metallurgical heating furnaces, халаалтын зуух хүртэл, calcium carbide furnaces, and calcium carbide furnaces. Electrofused mullite is widely used in metallurgical heating furnaces, халаалтын зуух хүртэл, кальцийн карбидын зуухны гаралтын, шилэн зуухны хана, гэх мэт.
PER Refractories produces standard refractory bricks and customized-shaped refractory bricks. High quality and cheap price are our advantages. You can contact us for a free quote in time.
Fused Cast Mullite Bricks Typical Physical Properies
| Al2O3 max (%) | 70-75 |
| SiO2 min (%) | 19-21 |
| Fe2O3 max (%) | 0.9-1.9 |
| Na2O max (%)a | 1.0-1.2 |
| True Specific Gravity | 3.54 g/cm |
| Хүйтэн бутлах хүч | 350 Мпа |
| Thermal Expansion at 1150℃ | 0.80% |
| Thermal Conductivity at 500-1500℃ | 4.6W/m.K |
| Сүвэрхэг чанар | 8% |
Composition of Fused Cast Mullite Bricks
Fused mullite generally includes high purity fused mullite and ordinary fused mullite. Compared with sintered fused mullite, fused mullite has coarse crystals of 1000 руу 2000. high-purity fused mullite is light gray, and ordinary fused mullite is dark gray (bauxite is the main raw material).
PER refractories factory can customize high purity fused mullite and ordinary fused mullite according to customers’ requirements. We also produce корунд муллит тоосго ба бусад types of refractory bricks.
Fused Cast Mullite Bricks are made of high alumina isotopes, composed of different alumina (3AL203.2Si02 mass fraction of AL2O372% and Si0228%). It is melted at about 2300°C and cast in a sand mold at 1850°C, then annealed to relieve stress.
The main crystalline phase is mullite and corundum, and the glass phase is filled between the crystalline phases. It is more resistant to glass liquid erosion than sintered refractories, but not as good as other electrofused refractories.
Adding a small amount of dioxygen (7%-8.5%) can make mullite crystals smaller, brick organization dense, mullite amount increased to 60%-70%, relatively reduce the glass phase content, reduce product cracks. Fused Cast Mullite Bricks have a low coefficient of thermal expansion, good resistance to thermal vibration, and strong resistance to glass liquid erosion.
Above 1450 ℃, mullite brick should not contact with alkali substances, otherwise it will make mullite decomposition. Mullite will also decompose in the reducing atmosphere above 1370℃, and part of Si02 becomes gaseous SiO to leave the brick body.
When the temperature is higher than 1650°C, even if the atmosphere is not restored, the mullite will decompose at a lower partial pressure of oxygen.
Fused Cast Mullite Bricks are made from high alumina isotopes, and different alumina is formulated to form the composition of mullite (3AL203-2Si02 mass fraction is: AL2O3 72%, Si02 28%). It is melted at about 2300°C, poured into the sand mold at thousand 1850°C, and then annealed to eliminate stress.
The main crystalline phase is mullite and corundum, the glass phase is filled in between the crystalline phase. Its resistance to glass liquid erosion is stronger than sintered refractories, but not as strong as other electrofusion refractories.
Add a small amount (7%-8.5%) of enamel dioxide, which can make the mullite crystals become a smaller, dense brick organization, the amount of mullite increased to 60%-70%, relatively reducing the content of the glass phase, and reduce the cracks of the products.
PER Refractories компанийн тухай
PER Refractories компани Шинми хотод байрладаг, Хэнань муж, Хятад дахь галд тэсвэртэй материалын өлгий нутаг. Манай компани нь технологид суурилсан галд тэсвэртэй үйлдвэр юм&Д, үйлдвэрлэл, борлуулалт, техникийн үйлчилгээ. Нутаг дэвсгэрийн баялаг нөөц, маш сайн чанар нь галд тэсвэртэй материал үйлдвэрлэх хосгүй дээд нөхцлийг бүрдүүлдэг.. Манай гол бүтээгдэхүүн бол галд тэсвэртэй шавар тоосго юм, өндөр хөнгөн цагааны исэлд тэсвэртэй тоосго, галд тэсвэртэй цахиурт тоосго, магнийн галд тэсвэртэй тоосго, муллит тоосго, тусгаарлагч тоосго, болон бусад өндөр температурт тэсвэртэй бүтээгдэхүүн.
PER хамгийн чухал зүйл гэж үздэг, Бид бүтээгдэхүүн бүрийг нухацтай авч, үйлчлүүлэгч бүрийг чин сэтгэлээсээ хүлээж авдаг гэдэгт итгэдэг. Бүх үйлчлүүлэгчиддээ хурдан бөгөөд чанартай үр дүнг өгөх. PER Refractories нь таны хамгийн найдвартай галд тэсвэртэй үйлдвэрлэгч, найдвартай түнш байх болно.
PER галд тэсвэртэй компани нь ногоон үйлдвэрлэлийн бааз юм, эрчим хүч хэмнэх, байгаль орчинд ээлтэй шинэ галд тэсвэртэй материал. Манай компани ISO9001 стандартыг давсан:2008 олон улсын чанарын системийн гэрчилгээ, GB/T24001-2004 / ISO14001:2004 байгаль орчны удирдлагын тогтолцооны гэрчилгээ, аж ахуйн нэгжийн чанарын хяналтын байгууллагын гэрчилгээ. Манай бүтээгдэхүүн илүү сайн борлуулагдаж байна 20 дэлхийн бүх улс орнууд. Эдгээр нь металлургийн хувьд илүүд үздэг галд тэсвэртэй бүтээгдэхүүн юм, өнгөт, нефть химийн, шил, керамик, болон бусад галд тэсвэртэй үйлдвэрүүд.