Batu-bata Cast Mullite Bercantum
Batu-bata Cast Mullite Bercantum are made of high-quality mullite clinker as raw material, which is melted and cast at high temperatures in an electric arc furnace.
The refractory fire bricks are characterized by dense crystal structure, suhu pelembutan beban tinggi, rintangan kejutan haba yang baik, high mechanical strength at room temperature and high temperature, good abrasion resistance, kekonduksian haba yang baik, and strong resistance to slag corrosion, dan lain-lain. The bricks are widely used in metallurgical heating furnaces, walaupun relau haba, calcium carbide furnaces, and calcium carbide furnaces. Electrofused mullite is widely used in metallurgical heating furnaces, walaupun relau haba, alur keluar relau kalsium karbida, dinding tanur kaca, dan sebagainya.
PER Refractories produces standard refractory bricks and customized-shaped refractory bricks. High quality and cheap price are our advantages. You can contact us for a free quote in time.
Fused Cast Mullite Bricks Typical Physical Properies
| Al2O3 max (%) | 70-75 |
| SiO2 min (%) | 19-21 |
| Fe2O3 max (%) | 0.9-1.9 |
| Na2O max (%)a | 1.0-1.2 |
| True Specific Gravity | 3.54 g/cm |
| Kekuatan Penghancuran Sejuk | 350 Mpa |
| Thermal Expansion at 1150℃ | 0.80% |
| Thermal Conductivity at 500-1500℃ | 4.6W/m.K |
| Keliangan | 8% |
Composition of Fused Cast Mullite Bricks
Fused mullite generally includes high purity fused mullite and ordinary fused mullite. Compared with sintered fused mullite, fused mullite has coarse crystals of 1000 kepada 2000. high-purity fused mullite is light gray, and ordinary fused mullite is dark gray (bauxite is the main raw material).
PER refractories factory can customize high purity fused mullite and ordinary fused mullite according to customers’ requirements. We also produce bata korundum mullite dan lain-lain types of refractory bricks.
Fused Cast Mullite Bricks are made of high alumina isotopes, composed of different alumina (3AL203.2Si02 mass fraction of AL2O372% and Si0228%). It is melted at about 2300°C and cast in a sand mold at 1850°C, then annealed to relieve stress.
The main crystalline phase is mullite and corundum, and the glass phase is filled between the crystalline phases. It is more resistant to glass liquid erosion than sintered refractories, but not as good as other electrofused refractories.
Adding a small amount of dioxygen (7%-8.5%) can make mullite crystals smaller, brick organization dense, mullite amount increased to 60%-70%, relatively reduce the glass phase content, reduce product cracks. Fused Cast Mullite Bricks have a low coefficient of thermal expansion, good resistance to thermal vibration, and strong resistance to glass liquid erosion.
Above 1450 ℃, mullite brick should not contact with alkali substances, otherwise it will make mullite decomposition. Mullite will also decompose in the reducing atmosphere above 1370℃, and part of Si02 becomes gaseous SiO to leave the brick body.
When the temperature is higher than 1650°C, even if the atmosphere is not restored, the mullite will decompose at a lower partial pressure of oxygen.
Fused Cast Mullite Bricks are made from high alumina isotopes, and different alumina is formulated to form the composition of mullite (3AL203-2Si02 mass fraction is: AL2O3 72%, Si02 28%). It is melted at about 2300°C, poured into the sand mold at thousand 1850°C, and then annealed to eliminate stress.
The main crystalline phase is mullite and corundum, the glass phase is filled in between the crystalline phase. Its resistance to glass liquid erosion is stronger than sintered refractories, but not as strong as other electrofusion refractories.
Add a small amount (7%-8.5%) of enamel dioxide, which can make the mullite crystals become a smaller, dense brick organization, the amount of mullite increased to 60%-70%, relatively reducing the content of the glass phase, and reduce the cracks of the products.
Mengenai Syarikat PER Refractory
Syarikat PER Refraktori terletak di Bandar Xinmi, Wilayah Henan, kampung halaman bahan refraktori di China. Syarikat kami ialah perusahaan refraktori berasaskan teknologi yang menyepadukan R&D, pengeluaran, jualan, dan perkhidmatan teknikal. Sumber yang kaya dan kualiti yang sangat baik di wilayah itu menyediakan keadaan unggul yang tiada tandingan untuk pengeluaran bahan tahan api. Produk utama kami ialah bata tanah liat tahan api, bata tahan api alumina tinggi, bata silika refraktori, bata tahan api magnesium, batu bata mullite, bata penebat, dan produk tahan suhu tinggi yang lain.
PER menganggap perkara yang paling penting, kami percaya dalam mengambil serius setiap produk dan menerima setiap pelanggan dengan ikhlas. Untuk memberikan hasil yang cepat dan berkualiti tinggi untuk semua pelanggan kami. PER Refraktori akan menjadi pengeluar refraktori anda yang paling boleh dipercayai dan rakan kongsi yang boleh dipercayai.
Syarikat PER refraktori adalah asas pengeluaran hijau, penjimatan tenaga, dan bahan refraktori baharu yang mesra alam. Syarikat kami telah lulus ISO9001:2008 pensijilan sistem kualiti antarabangsa dan GB/T24001-2004 / ISO14001:2004 pensijilan sistem pengurusan alam sekitar, pensijilan agensi pemeriksaan kualiti perusahaan. Produk kami dijual dengan baik dalam lebih daripada 20 negara di seluruh dunia. Mereka adalah produk refraktori pilihan untuk metalurgi, bukan ferus, petrokimia, kaca, seramik, dan industri refraktori lain.