Fire Clay Bricks For Sale
Fire Clay bricks is made of clay as the main raw material, which is mixed into plasticity and extruded by machinery. The extruded clay is called a brick billet, which is sent to the kiln after air-drying and calcined at a high temperature of 900-1000℃ to form bricks.
Clay bricks produced by PER Materiał ogniotrwały are commonly used in blast furnaces, gorące wielkie piece, piece szklarskie, piece ceramiczne, piece obrotowe, lime kilns, and other industrial kilns. Clay refractory brick products are generally divided into standard, common, and special, and can also be made according to user requirements. The common ones are common clay bricks and lightweight clay bricks. Welcome to buy cheap clay bricks from PER refractory brick manufacturers!
Characteristics Of Common Clay Bricks And Light Clay Bricks
Common Fire Clay Bricks
Nature: general term for clay refractories with regular shape. The main chemical composition is alumina and silicon dioxide, but it also contains the role of melting agent iron trioxide, calcium oxide, potassium oxide, sodium oxide, titanium dioxide, itp. Ordinary solid clay bricks are locally sourced, cheap, durable, and resistant to rapid cold and heat.
Clay bricks with dimensions of 240 mm x 115 mm x 53 mm. Each brick weighs approximately 2.5 Kg when dry and 3 Kg when water is absorbed.
Lightweight Fire Clay Bricks
Lightweight clay bricks are lightweight refractory products containing 30%-46% Al2O3. The main principle is clay clinker or light clinker and plastic clay. Usually produced by the combustible material method, but also by chemical method or foam method to form a porous structure. It is yellowish-brown in color. The bulk density of commonly used light clay bricks is 0.75-1.20g/cm3 compressive strength is 2.0-5.9MPa, and thermal conductivity is 0.221-0.442W/(M. K) (1350℃).
The Performance Of Clay Insulation Brick Produced by PRE Refractory
PER Refractories is a leading global refractory company with factories and sales. Our manufactured or customized clay bricks for kilns have many advantages. Również, we can offer cheap fire clay brick prices. Including:
1. Niska przewodność cieplna, with good thermal insulation and heat preservation effect.
2. Niska fuzja termiczna, due to low thermal conductivity.
3. Low impurity content has a very low content of oxides such as iron box alkali metal, W związku z tym, wysokie materiały ogniotrwałe, higher aluminum content allows it to maintain good performance under a reducing atmosphere.
4. Wysoka wytrzymałość na ściskanie w stanie gorącym.
5. Precyzyjny wygląd i rozmiar, speeding up masonry, reducing the use of refractory clay, ensuring the strength and stability of the masonry, przedłużając w ten sposób żywotność wykładziny
6. Can be processed into special shapes. To reduce the number of bricklaying blocks and masonry joints.
PER Refractory Have More Fire Clay Bricks Types
Clay Thermal Insulation Refractory Bricks
Fire clay thermal insulation refractory bricks are thermal insulation refractory products with 30%~48% Al2O3 content made of refractory clay as the main raw material.
Clay bricks are made of clinker clay, mixed, ukształtowany, wysuszony, sintered, and proportioned.
Clay brick thermal insulation brick is a weakly acidic refractory product, resistant to acid slag and gas erosion. It has poor resistance to alkaline compounds. Jednakże, it has good thermal shock performance.
It has the characteristics of corrosion resistance, odporność na zużycie, dobra odporność na szok termiczny, good splicing resistance, wysoka wytrzymałość mechaniczna, and good volume stability at high temperatures.
Clay bricks are most widely used in industrial kiln applications.
Fire Clay Bricks For Glass Kilns
The main component of clay bricks for glass melting kilns is AL2O3 content of 30~48% and SIO2 content of 50~70.
It is an acidic refractory material.
It can resist the erosion of acidic slag and acidic gas, and the resistance to alkaline material is slightly poor.
The refractoriness of this clay brick is not comparable to that of silicon brick, up to 1690~1730℃. But the load softening temperature is 200℃ lower than silicon brick.
This is because the clay brick contains nearly half of the low melting point amorphous glass phase in addition to the high refractoriness of mullite crystals.
This product is most widely used in glass melting kilns.
Fire Clay Three-Hole Refractory Bricks
Clay three-hole brick refers to light refractory products containing Al2o330%-46%, with clay clinker or light clinker and plasticized clay as the main principle.
Commonly used clay insulation bricks have a bulk density of 0.75-1.20g/cm3 compressive strength of 2.0-5.9MPa and thermal conductivity of 0.221-0.442W/(M. K) (1350℃).
Clay three-hole brick has a wide range of uses, mainly used in a variety of industrial kilns without contact with molten material and no erosion of the role of gas insulation layer materials, wykorzystanie temperatury 1200-1400 ℃.
It is mainly used in thermal boilers, glass furnaces, cement furnaces, fertilizer gas furnaces, wielkie piece, piece na gorące powietrze, coking furnaces, electric furnaces, and casting and steel casting bricks.
The product has excellent properties such as high refractoriness, dense bulk density, niska porowatość, excellent high temperature creep performance, and good volume stability.
Application Range Of Fire Clay Bricks
PER Refractory Produced Clay refractory bricks have a wide range of applications, mostly used in the thermal insulation layer of thermal equipment and industrial kiln protection.
It can be used in parts without strong high-temperature molten material erosion and scouring effect, some direct contact with the flame surface coated with a refractory coating to reduce the erosion by slag protection and furnace gas soot scouring, to reduce damage.
The working temperature of the product does not exceed the test temperature of the refired line change.
Definition Of Clay In Fire Clay Bricks
In line with the principle of being responsible to our customers, PER strictly controls the quality of clay insulation brick products.
Our factory ensures that the produced refractories can have good high-temperature resistance and strong slag resistance.
It can adapt to the actual boiler operating temperature of customers.
Excellent product quality is even more by the majority of new and old users have been praised and support. Welcome you to call for consultation and purchase.
PER refractories group will provide professional boiler renovation and construction solutions with a sincere service attitude.
In the past, most people would consider the definition of clay in clay bricks to be a natural decomposition product of rock. This statement, when taken as a definition of clay, has a more ambiguous meaning.
Strictly speaking, it is extremely incorrect, because this statement can be applied to other decomposition products of rocks as well.
It is analyzed by chemical analysis, observation, and thermal effects. It is known that clays differ in their chemical composition and physical properties depending on their origin and the environment in which they are produced, even in different parts of the same area, sometimes between the top and bottom layers of clay.
But all of them are mainly composed of alumina, and interspersed with a small but variable amount of other oxides.
It can be seen that the complex composition and inconsistent physical properties of clay in clay bricks make it difficult to develop a definition that is both easy to understand and concise in meaning.
The clay insulation brick manufactured by advanced and unique technology has the characteristics of high compressive strength and low thermal conductivity. When used, they can reduce the furnace wall’s heat capacity and improve the furnace’s thermal efficiency.
The clay bricks produced by the PER refractory factory are suitable for building heat insulation layers and furnace lining of industrial kilns and other thermal engineering equipment.
O firmie PER materiałów ogniotrwałych
Firma materiałów ogniotrwałych PER znajduje się w mieście Xinmi, Prowincja Henan, rodzinne miasto materiałów ogniotrwałych w Chinach. Nasza firma jest opartym na technologii przedsiębiorstwem zajmującym się materiałami ogniotrwałymi, integrującym R&D, produkcja, obroty, i serwis techniczny. Bogate zasoby tego terytorium i doskonała jakość zapewniają niezrównane, doskonałe warunki do produkcji materiałów ogniotrwałych. Naszymi głównymi produktami są cegły ogniotrwałe, cegły ogniotrwałe o wysokiej zawartości tlenku glinu, ogniotrwałe cegły krzemionkowe, cegły ogniotrwałe magnezowe, cegły mulitowe, cegły izolacyjne, i inne produkty odporne na wysokie temperatury.
Company PER Refractory is the production base of green, oszczędzanie energii, i przyjazne dla środowiska nowe materiały ogniotrwałe. Nasza firma przeszła ISO9001:2008 międzynarodowy certyfikat systemu jakości i GB/T24001-2004 / ISO14001:2004 certyfikacja systemu zarządzania środowiskowego, certyfikacja agencji kontroli jakości w przedsiębiorstwie. Nasze produkty są dobrze sprzedawane w ponad 20 krajów na całym świecie. Są to preferowane produkty ogniotrwałe w metalurgii, nieżelazne, petrochemiczny, szkło, ceramika, i inne przemysł ogniotrwały.